OXYGEN CONTROL ON NANOCRYSTAL-ALON FILMS BY REACTIVE GAS-TIMING TECHNIQUE R.F. MAGNETRON SPUTTERING AND ANNEALING EFF

 

The AlON films grown on Si(100) substrates by using radio frequency (r.f.) magnetron sputtering from high purity aluminum (99.999% Al) target with a novel reactive gas-timing technique. The 100 nm thick of AlON films were deposited with 200 watts r.f. power and the substrate temperature is maintained at room temperature by the technique of gas-timing which varying flow-in sequence of high purity of Ar (99.999%) and N2 (99.9999%) gases fed into the sputtering chamber at 10:90 (sec) ratio. The composition and crystal orientation of AlON films affected by gas-timing of Ar and N2 were analyzed by Auger Electron Spectroscopy (AES) and Xray diffraction (XRD). The oxygen atoms revealed by AES formed into a corporation in films was studied. This suggests that the oxygen contamination formed as AlOXNY compound may due to the residual oxygen in base pressure of 10-7 mbar and higher reactivity of oxygen in the reactor compared to nitrogen. The gas-timing technique used in the sputtering growth system shows the advantage of the oxygen quantity control, while the general sputtering process (without gas-timing technique) shows an increase of the oxygen composition depended on film thickness. The characterizations results clearly indicate that the gas-timing r.f. magnetron sputtering technique plays an important role to control the incorporation of oxygen and to form the nanocrystalaluminum oxynitride films which very attractive for various sensors applications.

 

 

Author editor

Post on 2009-06-14 | View 21906