AN EXTREME CHANGE IN STRUCTURAL AND OPTICAL PROPERTIES OF INDIUM OXYNITRIDE DEPOSITED BY REACTIVE GAS-TIMING RF MAGNETRO

 

The indium oxynitride (InON) films were achieved by reactive RF magnetron sputtering indium target which has the purity of 99.999% with a novel reactive gas-timing technique. The structural, optical and electrical properties in a series of polycrystalline InON films affected by gas-timing of reactive N₂ and O₂ gases introduced to the chamber were observed. The X-ray photoelectron spectroscopy revealed that the oxygen content in thin films that compounded to indium and nitrogen, which increased from 10% in indiumnitride (InN) to 66% in indiumoxide (In₂O₃) films. The X-ray diffraction peaks show that the phase of deposited films changes from InN to InON and to In₂O₃ with an increasing oxygen timing. The hexagonal structure of InN films with predominant (0 0 2) and (0 0 4) orientation was observed when pure nitrogen is only used as sputtering gas, while InON and In₂O₃ seem to demonstrate body-center cubic polycrystalline structures depending on gas-timing. The surface morphologies investigated from atomic force microscope of deposited films with varying gas-timing of O₂:N₂ show indifferent. The numerical algorithm method was used to define the optical bandgap of films from transmittance results. The increasing oxygen gas-timing affects extremely to the change of crystallinity phase from InN to InON and to In₂O₃, the increase of optical bandgap from 1.4 to 3.4 eV and the rise of sheet resistance from 15 Ω/sq. to insulator.

 

 

Author editor

Post on 2009-06-14 | View 23644